Bo-Eun Park, Il-Kwon Oh, Chandreswar Mahata, ChangWan Lee, David Thompson,
Han-Bo-Ram Lee, Wan Joo Maeng, Hyungjun Kim
Journal of Alloys and Compounds, Volume 722, October 2017 ,Pages 307-312
Doi : 10.1016/j.jallcom.2017.06.036
Abstract
With accelerated shrinking of integrated circuit, the fabrication of metal-insulator-metal (MIM) capacitors having a high capacitance density and low leakage current for dynamic random access memory (DRAM) has become a challenge. In this study, we investigated Y-stabilized ZrO2 as a novel high-k material for DRAM capacitors. We used atomic layer deposition (ALD) to produce Y-stabilized ZrO2; this technique enables easy control of the Y concentration by changing the ratio of ZrO2 to Y2O3 ALD cycles. This technique is suitable for future DRAM capacitors, as it provides superior thickness controllability and
conformality. Y doping into ZrO2 increases the oxygen vacancy content in the films and transforms the ZrO2 crystal structure from monoclinic to cubic. As a result, the dielectric constant is significantly increased from 19.1 to 30.2. Moreover, Y doping shifts the defect level into the conduction band rather than the energy bandgap, resulting in about 60 times lower leakage current density for Y-doped ZrO2 compared to undoped ZrO2. It is notable that the dielectric properties and the leakage current density are simultaneously enhanced, indicating that Y-doped ZrO2 is a promising candidate to satisfy the requirements of future DRAM capacitors.